Degradable ECO paper tape and its production process

Article provenance:未知 Popularity:Time:2020-05-14 22:34
Degradable kraft paper tape manufacturers introduced that packaging tape, also known as BOPP tape, case sealing tape, etc., is a roll adhesive tape made of BOPP, PVC, pet, PE and other plastic films as the base material, and then evenly coated with elastic type pressure-sensitive adhesive or resin type pressure-sensitive adhesive on the base material. It is an indispensable product in light industry enterprises, companies and personal life. The existing packaging tape generally includes release layer, base material layer and adhesive layer. At present, there are many kinds of packaging tape used in the market. When consumers dismantle and assemble the products, the packaging tape is thrown along with the packaging box. As we all know, for the general paper packaging tape, the cardboard can be recycled and reused, while the adhesive tape on the packaging box is torn As the existing base material layer is mostly BOPP, PVC, pet and PE plastic films, these plastic films are ordinary polypropylene plastic films, which are not degradable and have no recycling value, more inconvenient for recycling, and can only be directly turned into garbage. These ordinary polypropylene plastic waste films can not be decomposed within decades after the garbage is deeply buried, if they are recycled together with garbage Combustion treatment will also bring environmental pollution and harm to human health. Although there are some degradable packaging tapes in the existing market, after investigation, it is found that these tapes have the following conditions, either with environmental protection label, in fact, the materials used are the same as the existing packaging tapes; or they are made of degradable materials, But the strength of environmental protection tape is poor, it is easy to break in the process of bonding, the bonding strength is not ideal, and the adhesive and substrate layer are easy to fall off. Therefore, it is necessary to develop a kind of degradable environmental protection packaging tape with simple production method, easy to realize, low production cost, firm adhesion, innocuity, good mechanical strength and high degradation performance.
 
Technical implementation elements:
 
In order to solve the problems existing in the background technology, the invention aims to provide a degradable environmental protection packaging tape with simple production method, easy realization, low production cost, firm adhesion, innocuity and innocuity, good mechanical strength and high degradation performance, and a production method thereof.
 
The degradable environmental protection packaging tape includes a base material layer, a release layer and an adhesive layer. The base material layer includes an inner layer, a middle layer and an outer layer. The release layer is arranged on the outer layer, and the adhesive layer is arranged on the inner layer;
 
The outer film is formed by 60-80 parts of resin, 30-50 parts of esterified starch, 10-20 parts of medium density polyethylene, 5-15 parts of reinforcing agent, 1-5 parts of crosslinking agent and 0.5-1 parts of lubricant;
 
The middle layer film is formed by 40-60 parts of resin, 50-80 parts of esterified starch, 10-20 parts of medium density polyethylene, 5-15 parts of reinforcing agent, 1-5 parts of crosslinking agent and 0.5-1 parts of lubricant;
 
The inner layer film is formed by 60-80 parts of resin, 30-50 parts of esterified starch, 10-20 parts of low-density polyethylene, 5-15 parts of reinforcing agent, 1-5 parts of crosslinking agent and 0.5-1 parts of lubricant.
 
Wherein, the reinforcing agent is inorganic whisker material, the crosslinking agent is triallylisocyanurate and toluene diisocyanate, the mass ratio of triallylisocyanurate and toluene diisocyanate is 1:2-3, and the lubricant is paraffin.
 
The melt index of the medium density polyethylene is greater than 0.03g/min, and the density is 0.90-0.95g/cm3; the melt index of the low density polyethylene is greater than 0.3g/min, and the density is 0.90-0.95g/cm3.
 
The preparation method of esterified starch is as follows: firstly, the starch and water are mixed in the proportion of 1:100-120 to obtain the mixed solution, then the mixed solution is stirred at the speed of 2000-2500r / min for 15-20min to obtain the dispersing solution, and then the dispersing solution is added with the fermenting agent, which is put into the environment of 30-35 ℃ to ferment for 1-2h to obtain the fermenting solution, and the adding amount of the fermenting agent is the total amount of the dispersing solution 0.2-0.5% of the mass, and the said fermentation agent is hydrogen bacteria and Bacillus subtilis; finally, the esterified starch can be obtained by separating, washing and drying the fermentation liquid.
 
The production method of the degradable environmental protection packaging tape comprises the following steps:
 
① Preparation of the base material layer: first mix the inner layer film raw material, middle layer film raw material and outer layer film raw material in the mixing tank, then send the inner layer film raw material, middle layer film raw material and outer layer film raw material into the three-layer coextrusion blowing machine to extrude the blown film, and then roll the cooled film to obtain the base material layer. The extruding temperature of the outer layer film and inner layer film is 150-180 ℃, and the extruding temperature of the intermediate film is 150-180 ℃ The outlet temperature is 140-160 ℃, and the thickness ratio of the inner layer film, the middle layer film and the outer layer film is 1-2:2-3:1-2;
 
② Corona treatment: place the substrate layer made in step ① on the automatic unwinder for automatic unwinding, and then conduct corona treatment on the surface of the substrate layer through the corona treatment device;
 
③ Release: apply a layer of 1-2um thick release layer on the outer layer of the base material layer through the release mechanism, and then guide the base material layer coated with the release layer into the drying box through the guide roller. Cure the release layer through heating, and control the temperature in the drying box to 60-80 ℃. Finally, guide the base material layer after heating and solidifying into the cooling mechanism through the guide roller for cooling;
 
④ Coating: after leaving the mold, first use the guide roller to transfer the substrate layer to the coating mechanism, and then use the coating roller to evenly apply the adhesive on the substrate